tNew and different separators were investigated as alternatives to well-known ion exchange separatorssuch as Nafion and Cation Exchange membrane (CMI). In polarization tests, the maximum power den-sities of new separators without functional groups were comparatively higher than those of Nafion andCMI. The non-woven fabric Polypropylene (PP80) exhibited maximum voltage of 0.477 V (with 1000 ),which was similar to that of Nafion (0.481 V), and resulted in the highest power density of 121 mW/m2(Nafion; 118 mW/m2). Polypropylene 80 and 100 exhibited relatively smaller ohmic resistances of 11 and 2 , respectively, compared to others with resistances ranging from 13 to 41 . Concerning oxygendiffusion, all types of size selective separators exhibited high oxygen mass transfer compared to Nafionand CMI. This high oxygen diffusion was likely the reason for the lower columbic efficiencies (CE) of PP80(44%) and PP100 (42%) compared to Nafion (50%). PP80 exhibited a high proton mass transfer coefficient(KH= 11 × 10?5cm/s) compared to all ion exchange and size selective separators included in this study.These results suggest that low-cost separators could be used for field applications of MFCs for higher cellvoltage while minimizing oxygen diffusion.