The pH & alkalinity adjustment method by lime and carbon dioxide(CO2) for corrosion control in water distribution system was investigated to evaluate the corrosion characteristics of metal pipes, such as galvanized iron, copper, stainless steel, and carbon steel. When the pH in sand filtered and ozone+GAC treated water was increased with lime and CO2 from 7.5 to 8.0, the concentration of residual chlorine decreased at higher pH and longer reaction time; the concentration of trihalomethane increased. The corrosion rate of coupons with corrosion control using lime and carbon dioxide was showed much smaller than those without corrosion control using pilot-scale simulated distribution system. The galvanized iron was corroded much faster than carbon steel, copper, and stainless steel. Especially, copper and stainless steel coupons were hardly corroded. The galvanized iron and carbon steel coupons with corrosion control were produced the corrosion products less than those without corrosion control by the results of environmental scanning electron microscope(ESEM) and energy dispersive x-ray spectroscopy(EDS) analyses. The galvanized iron coupon with pH and alkalinity adjustment by lime and carbon dioxide was detected about 30 percent of zinc, when the carbon steel was detected about 30 percent of calcium by calcium carbonate products formation. For the results of X-ray diffraction(XRD) analysis, the goethite(α-FeOOH) was identified as primary corrosion product of galvanized iron without corrosion control, while the Zinc oxide(ZnO) was found on corrosion products of galvanized iron coupon with corrosion control as the results of EDS analysis. However, the carbon steel corrosion products regardless of corrosion control were composed predominantly of maghemite(γ-Fe2O3) and hematite(α-Fe2O3).